Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Ultramid® B3EG4 SI UN - PA6-GF20 - BASF

Check here, which other Ultramid B datasheets, application examples or technical articles are available in Material Data Center

Caracteristicas de procesamiento y fisicas - Propiedades mecánicas - Propiedades térmicas - Otras propiedades - Propiedades específicas del material - Funciones

Any use of this information falls under the rules of our disclaimer.

Texto del producto

Glass fibre-reinforced injection moulding grade, with excellent surface quality especially suitable for the production of visible parts. Optimum surface quality is generally obtained at a very high injection speed.

Caracteristicas de procesamiento y fisicas	Seco / Cond	Unidades	Método de ensayo
ISO Data
Indice de fluidez volumétrico, MVR	25 / *	cm³/10min	ISO 1133
Temperatura	275 / *	°C	-
Carga	5 / *	kg	-
Contracción posterior al moldeo, paralelo	0.4 / *	%	ISO 294-4, 2577
Contracción posterior al moldeo, normal	0.7 / *	%	ISO 294-4, 2577

Propiedades mecánicas	Seco / Cond	Unidades	Método de ensayo
ISO Data
Módulo de tracción	7150 / 3750	MPa	ISO 527
Resistencia a la tracción	150 / 80	MPa	ISO 527
Alargamiento a rotura	3.8 / 14	%	ISO 527
Resistencia al impacto Charpy, +23°C	65 / 100	kJ/m²	ISO 179/1eU
Resistencia al impacto Charpy, -30°C	55 / 55	kJ/m²	ISO 179/1eU
Resistencia al impacto Charpy c/entalla, +23°C	9 / 19	kJ/m²	ISO 179/1eA
Resistencia al impacto Charpy c/entalla, -30°C	7.5 / 7.5	kJ/m²	ISO 179/1eA

Propiedades térmicas	Seco / Cond	Unidades	Método de ensayo
ISO Data
Temperatura de fusión, 10°C/min	220 / *	°C	ISO 11357-1/-3
Estabilidad al calor, 1.80 MPa	200 / *	°C	ISO 75-1/-2
Estabilidad al calor, 0.45 MPa	215 / *	°C	ISO 75-1/-2

Otras propiedades	Seco / Cond	Unidades	Método de ensayo
Densidad	1270 / *	kg/m³	ISO 1183

Propiedades específicas del material	Seco / Cond	Unidades	Método de ensayo
ISO Data
Indice de viscosidad	148 / *	cm³/g	ISO 307, 1157, 1628

Funciones

Características

Procesamiento y forma de entrega

Moldeo por inyección

Forma de suministro

Sémola, Color natural

Aditivos

Desmoldeante

Disponibilidad regional

Norteamérica, Europa

Demás información

Moldeo por inyección

PREPROCESSING
Pre/Post-processing, max. allowed water content: .05 %
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 4 - 8 h

PROCESSING
injection molding, Melt temperature, range: 260 - 280 °C
injection molding, Melt temperature, recommended: 270 °C
injection molding, Mold temperature, range: 80 - 110 °C
injection molding, Mold temperature, recommended: 100 °C
injection molding, Dwell time, thermoplastics: 10 min

Resistencia a medios químicos

Acidos
	Ácido acético (5% por masa) (23°C)
	Solución ácido cítrico (10% por masa) (23°C)
	Ácido láctico (10% por masa) (23°C)
	Ácido clorhídrico (36% por masa) (23°C)
	Ácido nítrico (40% por masa) (23°C)
	Ácido sulfúrico (38% por masa) (23°C)
	Ácido sulfúrico (5% por masa) (23°C)
	Solución ácido crómico (40% por masa) (23°C)
Bases
	Solución de hidróxido de sodio (35% por masa) (23°C)
	Solución de hidróxido de sodio (1% por masa) (23°C)
Alcoholes
	Alcohol isopropílico (23°C)
	Metanol (23°C)
	Etanol (23°C)
Hidrocarburos
	N-hexano (23°C)
	Tolueno (23°C)
	Iso-octano (23°C)
Cetonas
	Acetona (23°C)
Éteres
	Dietil éter (23°C)
Soluciones de sal
	Solución de cloruro de sodio (10% por masa) (23°C)
	Solución de hipoclorito de sodio (10% por masa) (23°C)
	Solución de cloruro de cinc (50% por masa) (23°C)
Otros
	Acetato etílico (23°C)
	Agua oxigenada (23°C)
	Glicol etilénico (50% por masa) en agua (108°C)
	Agua (23°C)

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com